Heterogeneous substrate bonding for photonic integration

ABSTRACT

A method of fabricating a composite integrated optical device includes providing a substrate comprising a silicon layer, forming a waveguide in the silicon layer, and forming a layer comprising a metal material coupled to the silicon layer. The method also includes providing an optical detector, forming a metal-assisted bond between the metal material and a first portion of the optical detector, forming a direct semiconductor-semiconductor bond between the waveguide, and a second portion of the optical detector.

CROSS-REFERENCES TO RELATED APPLICATIONS

This application is a continuation of U.S. patent application Ser. No. 16/452,212, filed on Jun. 25, 2019, entitled “METHOD AND SYSTEM FOR HETEROGENEOUS SUBSTRATE BONDING FOR PHOTONIC INTEGRATION,” which is a continuation of U.S. patent application Ser. No. 15/633,343, filed on Jun. 26, 2017, entitled “METHOD AND SYSTEM FOR HETEROGENEOUS SUBSTRATE BONDING FOR PHOTONIC INTEGRATION,” which application is a continuation of U.S. patent application Ser. No. 14/880,936, filed on Oct. 12, 2015, entitled “METHOD AND SYSTEM FOR HETEROGENEOUS SUBSTRATE BONDING FOR PHOTONIC INTEGRATION,” now U.S. Pat. No. 9,709,735, issued on Jul. 18, 2017, which application is a continuation of U.S. patent application Ser. No. 14/135,006, filed on Dec. 19, 2013, entitled “METHOD AND SYSTEM FOR HETEROGENEOUS SUBSTRATE BONDING FOR PHOTONIC INTEGRATION,” now U.S. Pat. No. 9,190,400, issued on No. 17, 2015, which application is a division of U.S. patent application Ser. No. 12/902,621, filed on Oct. 12, 2010, entitled “METHOD AND SYSTEM OF HETEROGENEOUS SUBSTRATE BONDING FOR PHOTONIC INTEGRATION,” now U.S. Pat. No. 8,630,326, issued on Jan. 14, 2014, which application claims priority to U.S. Provisional Patent Application No. 61/251,132, filed on Oct. 13, 2009, entitled “HETEROGENEOUS WAFER BONDING FOR PHOTONIC INTEGRATION.” The disclosures of all of the above-identified applications are hereby incorporated by reference in their entireties for all purposes. Additionally, the disclosure of U.S. Pat. No. 8,611,388 is hereby incorporated by reference in its entirety for all purposes.

BACKGROUND OF THE INVENTION

Silicon integrated circuits (“ICs”) have dominated the development of electronics and many technologies based upon silicon processing have been developed over the years. Their continued refinement led to nanoscale feature sizes that can be critical for making complementary metal oxide semiconductor CMOS circuits. On the other hand, silicon is not a direct bandgap materials. Although direct bandgap materials, including III-V compound semiconductor materials, such as indium phosphide, have been developed, there is a need in the art for improved methods and systems related to photonic ICs utilizing silicon substrates.

SUMMARY OF THE INVENTION

According to an embodiment of the present invention, techniques related to semiconductor fabrication processes are provided. Merely by way of example, embodiments of the present invention have been applied to methods and systems for bonding heterogeneous substrates for use in photonic integration applications. More particularly, an embodiment of the present invention utilizes a hybrid bonding structure including a metal/semiconductor bond and a semiconductor/semiconductor bond in order to achieve low optical loss and high electrical conductivity. The semiconductor/semiconductor bond may be an interface assisted bond. However, the scope of the present invention is broader than this application and includes other substrate bonding techniques.

According to an embodiment of the present invention, a hybrid integrated optical device is provided. The hybrid integrated optical device includes a substrate including a silicon layer and a compound semiconductor device bonded to the silicon layer. The hybrid integrated optical device also includes a bonding region disposed between the silicon layer and the compound semiconductor device. The bonding region includes a metal-semiconductor bond at a first portion of the bonding region. The metal-semiconductor bond includes a first pad bonded to the silicon layer, a bonding metal bonded to the first pad, and a second pad bonded to the bonding metal and the compound semiconductor device. The bonding region also includes an interface assisted bond at a second portion of the bonding region. The interface assisted bond includes an interface layer positioned between the silicon layer and the compound semiconductor device. The interface assisted bond provides an ohmic contact between the silicon layer and the compound semiconductor device.

According to another embodiment of the present invention, a method of fabricating a hybrid integrated optical device is provided. The method includes providing a substrate comprising a silicon layer and providing a compound semiconductor device. The method also includes forming a bonding region disposed between the silicon layer and the compound semiconductor device. The bonding region includes a metal-semiconductor bond at a first portion of the bonding region. The metal-semiconductor bond includes a first pad bonded to the silicon layer, a bonding metal bonded to the first pad, and a second pad bonded to the bonding metal and the compound semiconductor device. The bonding region also includes an interface assisted bond at a second portion of the bonding region. The interface assisted bond includes an interface layer positioned between the silicon layer and the compound semiconductor device, wherein the interface assisted bond provides an ohmic contact between the silicon layer and the compound semiconductor device.

Numerous benefits are achieved by way of the present invention over conventional techniques. For example, embodiments of the present invention provide methods and systems suitable for providing a bond with good mechanical strength, good electrical conductivity, sufficient compliance to allow the composite or hybrid bonding of semiconductor materials with different coefficients of thermal expansion with good reliability, and which also has good optical transparency. This combination of benefits allows both electrical and optical functionality across the bonded interface between two or more distinct semiconductor materials. These and other embodiments of the invention along with many of its advantages and features are described in more detail in conjunction with the text below and attached figures.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 illustrates an example of a photodiode with a low stress bond between a III-V substrate and a silicon substrate;

FIG. 2 illustrates a bonded structure according to an embodiment of the present invention;

FIG. 3 illustrates a phase diagram showing alloy stability according to an embodiment of the present invention;

FIG. 4 is a simplified schematic diagram of a compound semiconductor structure bonded to a silicon substrate according to an embodiment of the present invention;

FIGS. 5A-5C are simplified schematic diagrams illustrating bond interfaces according to an embodiment of the present invention;

FIGS. 6A-6B are simplified schematic diagrams illustrating bond interfaces according to another embodiment of the present invention;

FIG. 7 is a simplified flowchart illustrating a method of fabricating a hybrid semiconductor structure according to an embodiment of the present invention; and

FIG. 8 is a simplified flowchart illustrating a method of fabricating a hybrid semiconductor structure according to another embodiment of the present invention.

DETAILED DESCRIPTION OF SPECIFIC EMBODIMENTS

Embodiments of the present invention relate to an apparatus and method that preferably uses a bonding stress for wafer bonding and utilizes an intermediate layer to facilitate the transition from silicon and the like to another material for optical coupling as well as electron transport. Embodiments of the present invention preferably incorporate low stress, low temperature wafer bonding known in the industry and preferably comprise a thin film intermediate layer for optical coupling as well electron transport.

FIG. 1 illustrates an example of a photodiode with a low stress bond between a III-V substrate and a silicon substrate. FIG. 2 illustrates a bonded structure according to an embodiment of the present invention. As illustrated in FIG. 2 , two interfaces 712 and 714 are provided. First interface 712 is positioned between a silicon substrate 720 and an intermediate layer 718. Second interface 714 is located between intermediate layer 718 and a second semiconductor layer 716. Embodiments of the present invention are preferably used in the bonding process to facilitate integration of heterogeneous materials. Embodiments that facilitate integration preferably share the stress due to lattice mismatch between the silicon crystal and the second semiconductor that can form at these two interfaces and can be greatly reduced because of the reduced need for crystalline in the intermediate layer. The intermediate layer can be an alloy whose composition can be graded across the layer to facilitate the bonding at both interfaces 712 and 714.

Intermediate layer 718 is preferably thin, ranging from between approximately 4-5 monolayers to more than approximately 60-70 monolayers, substantially allowing the optical and thermal conduction properties to be virtually unaffected while the electron transport can preferably be achieved via actual carrier transport across the layer. In some embodiments of the present invention, intermediate layer 718 forms thermal and electric contacts at both the first interface and second interface. Embodiments of the present invention can be used in the fabrication of a plurality of high performance optoelectronic components, including but not limited to modulators, lasers, detectors, amplifiers, couplers, wavelength tunable optical components and/or circuits, combinations thereof, or the like. Embodiments as described herein are applicable to a variety of material systems including silicon as illustrated by silicon substrate 720 and/or the like and second semiconductor materials 716, which can be a compound semiconductor material. Utilizing embodiments of the present invention, heterogeneous materials (e.g., compound semiconductors and silicon substrates can be integrated on a common substrate.

The term “bandgap” as used throughout this application includes but is not limited to the energy difference between the top of the valence band and the bottom of the conduction band. The term “optical coupling” as used throughout this application includes but is not limited to placing two or more electromagnetic elements including optical waveguides close together so that the evanescent field generated by one element does not decay much before it reaches the other element. The term “electron transport” as used throughout this application includes but is not limited to an electron transport chain coupling a chemical reaction between an electron donor and an electron acceptor to the transfer of H⁺ ions across a membrane, through a set of mediating chemical or biochemical reactions. The term “complementary metal oxide semiconductor” as used throughout this application includes but is not limited to technologies for making integrated circuits, microprocessors, microcontrollers, static RAM, digital logic circuits, analog circuits, and highly integrated transceivers.

Embodiments of the present invention optionally utilize several features of intermediate layer 718 as illustrated in FIG. 2 . According to an embodiment, the thickness of the intermediate layer 718 is very thin, ranging from a few monolayers (i.e., around 10 Å in thickness) to tens of monolayers. In an embodiment, the intermediate layer is deposited using a deposition technique that provides for uniform coverage at small thicknesses. Exemplary deposition techniques include PVD, ALD, sputtering, e-beam deposition, or the like. Intermediate layer 718 is preferably deposited at relatively low temperatures ranging from temperatures less than 200° C. At these low temperatures, there preferably exist small differences of thermal expansion (i.e., differences in the coefficient of thermal expansion (CTE)) between first interface 712 and second interface 714. Intermediate layer 718 preferably forms thermal contacts at the interfaces and is preferably thermally conductive. Intermediate layer 718 preferably forms good electrical contacts at both interfaces and is preferably electrically conductive. It is not necessary to be crystalline in nature so that the lattice matching at both interfaces is not an issue. In some embodiments, intermediate layer 718 is an alloy material for which the composition varies across the layer.

Embodiments of the present invention are applicable to an apparatus that includes a semiconductor layer that is provided over an intermediate layer that is provided over a silicon substrate layer. The intermediate layer has a lower thermal conductivity than the semiconductor layer. The apparatus also includes a plurality of interfaces that are provided between the semiconductor layer and the underlying layer(s), thereby preventing crystalline lattice mismatch.

Embodiments of the present invention also include a bonding method including forming first and second bonding surfaces on first and second materials, respectively, at least one of the bonding surfaces including an intermediate layer. The method also includes enhancing activation of at least one of said first and second bonding surfaces, terminating at least one of said first and second bonding surfaces with species allowing formation of chemical and electrical bonds, and annealing said first and second materials at a temperature.

FIG. 3 illustrates a phase diagram showing alloy stability according to an embodiment of the present invention. As illustrated in FIG. 3 , the stability of the alloy makes such an alloy suitable for use as an intermediate layer such as intermediate layer 718. In some embodiments, the alloy (e.g., In_(x)Pd_(y)) has a small thickness to accommodate stress at the semiconductor-semiconductor interface.

While the embodiments of the invention described herein are directed to wafers used in the semiconductor industry, the invention is also applicable to thermoelectric (TE) cooling technology as well as virtually any application including optical coupling and electron transport.

Merely by way of example, an intermediate layer suitable for use according to embodiments of the present invention is In_(x)Pd_(y), for example, In_(0.7)Pd_(0.3), which is an alloy that is stable up to very high temperatures as illustrated in FIG. 3 . This alloy forms an ohmic contact at interfaces with both silicon and/or III-V materials for which the doping types at either side can be either p-type or n-type. Thus, embodiments of the present invention provide an intermediate layer that provides both ohmic contact between materials on both sides of the intermediate layer, adhesion, optical quality including transparency (i.e., low optical loss), stress accommodation, and other benefits. Other suitable alloys include germanium palladium, gold/germanium, Au/Sn, Al/Mg, Au/Si, palladium, indium/tin/silver alloys, metal alloys containing Bi, Sn, Zn, Pb, or In, combinations thereof, or the like. The optimal alloy will generally have eutectic or peritectic points, and will allow a bonding process temperature in the 350° C. to 500° C. range.

FIG. 4 is a simplified schematic diagram of a compound semiconductor structure bonded to a silicon substrate according to an embodiment of the present invention. Referring to FIG. 4 , a composite metal/semiconductor bond is illustrated in relation to bonding of a compound semiconductor device 810 to a silicon-based substrate 805. In the embodiment illustrated in FIG. 4 , the silicon-based substrate 805 is a silicon-on-insulator (SOI) substrate although this is not required by embodiments of the present invention. The SOI substrate includes a silicon handle layer 806, a silicon oxide layer 807, and a silicon layer 808, which may be single crystal silicon. Planarizing material is used in the embodiment illustrated in FIG. 4 as well as an interconnect metal that provides for electrical conductivity between portions of the compound semiconductor device 810 and the silicon layer 808 of the SOI substrate. In the embodiment illustrated in FIG. 4 , the compound semiconductor device 810 extends to a height above the top surface of the silicon layer 808.

As illustrated in FIG. 4 , several bonds are formed between silicon layer 808 and the compound semiconductor device 810. Bond 1 is a metal/metal bond. Associated with Bond 1, pads (not shown in FIG. 4 but illustrated in following figures) are defined on both the SOI substrate (e.g., silicon layer 808) and the compound semiconductor device 810. These pads can include an adhesion metal such as Ti or Cr and a barrier metal such as Pt or Ni. The metal used for the bonding process will typically be a eutectic solder with a eutectic point in the 350° C.-500° C. range. An example of such a eutectic solder is AuGe.

Bond 2 as illustrated in FIG. 4 can be either a direct semiconductor/semiconductor bond or a metal-assisted semiconductor/semiconductor bond. For the metal-assisted semiconductor/semiconductor bond, a thin metal layer (e.g., ranging from one to a few monolayers to a few tens of monolayers) is deposited to improve the robustness of the interface and to better accommodate the CTE differences between silicon and the compound semiconductor device. In an embodiment, the thin metal layer is less than 50 Å in thickness. The very thin interfacial metal will still allow light to pass through without significant attenuation. The direct semiconductor/semiconductor bond can be formed using techniques including either chemical activation or plasma activation of the surfaces and joining the materials together with pressure and low temperature in order to bond the two surfaces together. Direct semiconductor bonding is useful in devices employing evanescent coupling in a waveguide structure as it will have lower optical attenuation than metal-assisted semiconductor bonding.

FIGS. 5A-5C are simplified schematic diagrams illustrating bond interfaces according to an embodiment of the present invention. As illustrated in FIG. 5A, the compound semiconductor device 820 has been thinned so that the top surface of the compound semiconductor device 820 is coplanar with the top surface of silicon layer 808. A planarizing material has been used to provide a planar surface extending above the top surface of silicon layer 808. Portions of the planarizing material have been removed (e.g., using a masking and etching process) and interconnect metals have been used to provide for electrical connectivity between portions of the silicon layer 808 and portions of the compound semiconductor device 820.

FIG. 5B illustrates additional details related to Bond 1 including pads 830 and 832 that provide for adhesion between the silicon layer 808, the bonding metal 834 and the compound semiconductor device 820. As discussed in relation to FIG. 4 , pads 830 and 832 can include an adhesion metal such as Ti or Cr and a barrier metal such as Pt. The bonding metal 834 can be a eutectic solder such as AuGe. Other pad materials include Ni, W, refractory metals used as barrier layers in silicon-based devices, or the like, and other bonding metals include AuSn, InPd, InSn, InSnAg alloys, combinations thereof, or the like. These materials are listed merely by way of example and other materials that provide for adhesion between surfaces and/or barrier functionality are also included within the scope of the present invention.

FIG. 5C illustrates the use of an interface layer 840 between the compound semiconductor device 820 and the silicon layer 808. As discussed previously, the metal-assisted semiconductor/semiconductor bond illustrated in FIG. 5C includes a thin metal layer that provides beneficial functions including improving the robustness of the interface and accommodating CTE differences between the materials bonded to either side of this interface layer. Interface layers can include suitable materials including materials that provide peritectic properties including metals such as InPd, other metal alloys, combinations thereof, or the like. Gettering materials such as Ti or Cr can also be integrated with the interface layer to getter surface oxides and improve bond properties. For thin layers of interfacial metals, light will be able to pass without significant attenuation. The low optical loss provided by embodiments of the present invention include absorption coefficients that can be computed using waveguide models and the measured absorption properties of the interface layer. The use of an interface layer 840 will also provide an ohmic contact between the silicon layer 808 and the compound semiconductor device 820. Thus, embodiments of the present invention provide an interface that is electrically conductive without significant optical absorption.

Although FIGS. 5A-5C illustrate bonding of a compound semiconductor device to an SOI substrate, embodiments of the present invention are not limited to the bonding of a device to a substrate. Other embodiments of the present invention are applicable to substrate to substrate bonding, also referred to as wafer bonding. Thus, the compound semiconductor device illustrated in the figures can be replaced with a compound semiconductor substrate in the processes and structures described herein. One of ordinary skill in the art would recognize many variations, modifications, and alternatives.

As illustrated in FIG. 5C, an interface layer 840 such as a thin layer (e.g., less than 100 Å) of a metal alloy such as In_(x)Pd_(y), can be used to accommodate some of the CTE mismatch between the two semiconductor materials. In other embodiments, the interface layer is not present and a direct semiconductor/semiconductor bond is formed for Bond 2. Embodiments of the present invention utilize both a metal/metal bond illustrated by Bond 1 and a direct semiconductor/semiconductor bond or an interface assisted semiconductor/semiconductor bond illustrated by Bond 2. Such a hybrid bonding approach utilizes the benefits provided by both types of bonds to reduce or overcome the disadvantages of low temperature semiconductor/semiconductor bonding including the weak interface as well as the disadvantages of metal/metal bonding including high optical loss in the vicinity of the metal/metal bond. Thus, embodiments of the present invention provide for high strength bonds and electrical conductivity (Bond 1) while enabling low optical loss and electrical conductivity in regions of the structure suitable for light propagation (Bond 2).

FIGS. 6A-6B are simplified schematic diagrams illustrating bond interfaces according to another embodiment of the present invention. In the case where light propagates parallel to the interface formed at Bond 2 and evanescent coupling is used between the silicon layer 808 and the compound semiconductor device 820, a combination of direct semiconductor-semiconductor bonding and metal-assisted semiconductor-semiconductor bonding may be employed to form Bond 2. This can be achieved by selective patterning of the thin interfacial metal. Referring to FIG. 6A, Bond 2′ between the silicon layer 808 and the compound semiconductor device 810 is illustrated. Bond 2′ includes not only an interface layer 840′ similar to layer 840 in FIG. 5C, but a direct semiconductor-semiconductor bond 842. In the embodiment illustrated in FIG. 6B, the interface layer 840′ is patterned to provide regions that are free of the interface layer, which may be a metal layer. As an example, in a light emitting device, the direct semiconductor-semiconductor bond could be positioned adjacent the light emission region to prevent absorption of light by the interface layer. The combination of an interface layer with a direct semiconductor-semiconductor bond thus provides benefits associated with each of the bonding techniques in a hybrid manner.

The bonding processes described herein can be performed in the temperature range from about 350° C. to about 500° C. In a particular embodiment, the temperature associated with the bonding process is in the temperature range of 400° C.-450° C. These temperatures are below the temperature at which CMOS circuits, which may be previously fabricated on the SOI substrate, would be damaged. This enables the integration of complex electrical functions while still providing a robust bond between the dissimilar materials discussed herein.

FIG. 7 is a simplified flowchart illustrating a method of fabricating a hybrid semiconductor structure according to an embodiment of the present invention. The method 900 includes providing a substrate comprising a silicon layer (910), providing a compound semiconductor device (e.g., an InP semiconductor laser) (912), and forming a bonding region disposed between the silicon layer and the compound semiconductor device. Forming the bonding region includes forming a metal-semiconductor bond at a first portion of the bonding region (914). The metal-semiconductor bond includes a first pad bonded to the silicon layer, a bonding metal bonded to the first pad, and a second pad bonded to the bonding metal and the compound semiconductor device. Forming the bonding region also includes forming an interface assisted bond at a second portion of the bonding region (916). The interface assisted bond includes an interface layer (e.g., In_(x)Pd_(y)) positioned between the silicon layer and the compound semiconductor device. The interface assisted bond provides an ohmic contact between the silicon layer and the compound semiconductor device. In an embodiment, the interface layer has a thickness less than 50 Å.

According to an embodiment, the substrate includes an SOI wafer including a silicon substrate, an oxide layer disposed on the silicon substrate, and the silicon layer is disposed on the oxide layer. In embodiments utilizing a laser or other light generator, the second portion of the bonding region can be substantially free from the interface layer at a position adjacent an active region of the laser or optical generator in order to reduce optical losses. The bonding processes can be performed using low temperature bonding processes, for example, at a temperature ranging from about 350° C. to about 500° C., more particularly, from about 400° C. to about 450° C.

It should be appreciated that the specific steps illustrated in FIG. 7 provide a particular method of fabricating a hybrid semiconductor structure according to an embodiment of the present invention. Other sequences of steps may also be performed according to alternative embodiments. For example, alternative embodiments of the present invention may perform the steps outlined above in a different order. Moreover, the individual steps illustrated in FIG. 7 may include multiple sub-steps that may be performed in various sequences as appropriate to the individual step. Furthermore, additional steps may be added or removed depending on the particular applications. One of ordinary skill in the art would recognize many variations, modifications, and alternatives.

FIG. 8 is a simplified flowchart illustrating a method of fabricating a hybrid semiconductor structure according to another embodiment of the present invention. The method 950 includes providing an SOI substrate (960) and providing a compound semiconductor device (962), which can also be referred to as a compound semiconductor die. In an embodiment of the present invention, the SOI substrate includes one or more optical components such as waveguides, optical isolators, reflective structures, or the like and the compound semiconductor device is an InP gain medium.

The method also includes patterning metals in a first bond region (964). The metals can be deposited or formed in a variety of manners. The first bond region can be used for metal-metal bonding and/or for metal-assisted semiconductor-semiconductor bond on one or both materials. After the metals are patterned, a surface treatment is performed (966), for example, a chemical treatment of the surface(s), a plasma activation for a semiconductor-semiconductor bond without metal assist, or the like. The surface treatment can be performed in a controlled atmosphere such as an inert environment, a reduced pressure atmosphere such as a vacuum, or the like. The method further includes positioning the compound semiconductor device on the SOI substrate, such as a receptor site (968) and applying heat and pressure to join the compound semiconductor device to the SOI substrate (970). In an embodiment, the joining step simultaneously effects both metal-based and semiconductor-based bonds.

It should be appreciated that the specific steps illustrated in FIG. 8 provide a particular method of fabricating a hybrid semiconductor structure according to another embodiment of the present invention. Other sequences of steps may also be performed according to alternative embodiments. For example, alternative embodiments of the present invention may perform the steps outlined above in a different order. Moreover, the individual steps illustrated in FIG. 8 may include multiple sub-steps that may be performed in various sequences as appropriate to the individual step. Furthermore, additional steps may be added or removed depending on the particular applications. One of ordinary skill in the art would recognize many variations, modifications, and alternatives.

It is also understood that the examples and embodiments described herein are for illustrative purposes only and that various modifications or changes in light thereof will be suggested to persons skilled in the art and are to be included within the spirit and purview of this application and scope of the appended claims. 

1. (canceled)
 2. A method of forming an integrated optical device, comprising: providing a substrate that forms: an uppermost substrate surface, and a recess within the uppermost substrate surface, the recess forming a lower substrate surface, the lower substrate surface and the uppermost substrate surface defining a recess height therebetween, and wherein one or more first metal pads are deposited on the lower substrate surface within the recess; providing a compound semiconductor device, comprising a portion of compound semiconductor material, wherein: the portion of the compound semiconductor material forms a planar uppermost surface, a planar lowermost surface, and a lower device surface that is parallel with the planar lowermost surface, the planar uppermost surface and the planar lowermost surface defining a device height therebetween, wherein the device height exceeds the recess height, and one or more second metal pads are deposited on the lower device surface; and bonding the one or more first metal pads to respective ones of the one or more second metal pads, with respective portions of a bonding metal, such that after the bonding and before subsequent processing, a height of the planar uppermost surface of the compound semiconductor device exceeds a height of the uppermost substrate surface.
 3. The method of claim 2, further comprising depositing a planarizing material that fills at least a portion of the recess that is not occupied by: the compound semiconductor device, the one or more first metal pads, the one or more second metal pads, and the bonding metal.
 4. The method of claim 3, wherein depositing the planarizing material comprises: depositing the planarizing material to a height above the lower substrate surface that exceeds a height of the uppermost surface of the portion of the compound semiconductor material above the lower substrate surface; and covering the uppermost surface of the compound semiconductor device with the planarizing material.
 5. The method of claim 4, furthermore comprising: forming one or more openings through the planarizing material; and forming interconnect metal to couple with at least one of: the uppermost substrate surface, or the planar uppermost surface of the portion of the compound semiconductor material, through the one or more openings.
 6. The method of claim 5, wherein forming the interconnect metal comprises forming at least one portion of the interconnect metal that connects the uppermost substrate surface with the planar uppermost surface of the portion of the compound semiconductor material, through respective ones of the one or more openings.
 7. The method of claim 2, wherein bonding the one or more first metal pads to the respective ones of the one or more second metal pads comprises providing In_(x)Pd_(y) as the bonding metal.
 8. The method of claim 7, wherein providing In_(x)Pd_(y) as the bonding metal comprises providing In_(0.7)Pd_(0.3) as the bonding metal.
 9. A method of forming an integrated optical device, comprising: providing a substrate that forms: an upper substrate surface, and a recess within the upper substrate surface, the recess forming a lower substrate surface, the lower substrate surface and the upper substrate surface defining a recess height therebetween, and wherein one or more first metal pads are deposited on the lower substrate surface within the recess; providing a compound semiconductor device comprising an upper device surface and a lower device surface, wherein: the upper device surface and the lower device surface define a device height therebetween, the device height exceeds the recess height, and one or more second metal pads are deposited on the lower device surface; and bonding the one or more first metal pads to respective ones of the one or more second metal pads, with respective portions of a bonding metal, such that after the bonding, and before subsequent processing, a height of the upper device surface of the compound semiconductor device exceeds a height of the upper substrate surface.
 10. The method of claim 9, further comprising depositing a planarizing material that fills at least a portion of the recess that is not occupied by: the compound semiconductor device, the one or more first metal pads, the one or more second metal pads, and the bonding metal.
 11. The method of claim 9, wherein bonding the one or more first metal pads to the respective ones of the one or more second metal pads comprises providing In_(x)Pd_(y) as the bonding metal.
 12. The method of claim 11, wherein providing In_(x)Pd_(y) as the bonding metal comprises providing In_(0.7)Pd_(0.3) as the bonding metal.
 13. The method of claim 9, wherein the one or more first metal pads or the one or more second metal pads comprise at least one of Ti, Cr, Pt, Ni or W.
 14. The method of claim 9, wherein: the substrate comprises a waveguide; the compound semiconductor device is configured to emit light; and the compound semiconductor device and the substrate are arranged to couple the light emitted by the compound semiconductor device into the waveguide.
 15. The method of claim 9, wherein the compound semiconductor device is configured to emit light.
 16. The method of claim 9, wherein: the compound semiconductor device has a lowermost surface, which is lower than the lower device surface; and the substrate and the compound semiconductor device form a direct semiconductor/semiconductor contact between the lower substrate surface and the lowermost device surface of the compound semiconductor device.
 17. The method of claim 9, wherein the compound semiconductor device is a detector.
 18. A method of forming an integrated optical device, comprising: providing a substrate that forms: an upper substrate surface, and a recess within the upper substrate surface, the recess forming a lower substrate surface, the lower substrate surface and the upper substrate surface defining a recess height therebetween, and wherein one or more first metal pads are deposited on to the lower substrate surface within the recess; providing a compound semiconductor device comprising an upper device surface and a lower device surface, wherein: the upper device surface and the lower device surface define a device height therebetween, and one or more second metal pads are deposited on to the lower device surface; and bonding the one or more first metal pads to respective ones of the one or more second metal pads, with respective portions of a bonding metal, wherein the bonding metal comprises In_(x)Pd_(y).
 19. The method of claim 18, wherein: the device height exceeds the recess height, and after the bonding, and before subsequent processing, a height of the upper device surface of the compound semiconductor device exceeds a height of the upper substrate surface.
 20. The method of claim 18, wherein: the substrate comprises a waveguide; the compound semiconductor device is configured to emit light; and the compound semiconductor device and the substrate are arranged to couple the light emitted by the compound semiconductor device into the waveguide.
 21. The method of claim 18, wherein the waveguide is a silicon waveguide. 